Surface texturing, either in combination with an anti-reflection coating or by itself, can also be used to minimise reflection. Any "roughening" of the surface reduces reflection by increasing the chances of reflected light bouncing back onto the surface, rather than out to the surrounding air.

Surface texturing can be accomplished in a number of ways. A single crystalline substrate can betextured by etching along the faces of the crystal planes. The crystalline structure of silicon results in a surface made up of pyramids if the surface is appropriately aligned with respect to the internal atoms. One such pyramid is illustrated in the drawing below. An electron microscope photograph of a textured silicon surface is shown in the photograph below. This type of texturing is called "random pyramid" texture, and is commonly used in industry for single crystalline wafers.

A square based pyramid which forms the surface of an appropriately textured crystalline silicon solar cell.

Scanning electron microscope photograph of a textured silicon surface.

Another type of surface texturing used is known as "inverted pyramid" texturing. Using this texturing scheme, the pyramids are etched down into the silicon surface rather than etched pointing upwards from the surface. A photograph of such a textured surface is shown below.

Scanning electron microscope photograph of a textured silicon surface.

Multicrystalline wafers cannot be textured by using either of the above methods since effective surface morphology can only be achieved when the top surface consists of an exposed <111> crystal plane. For multicrystalline wafers, only a small fraction of the surface will have the required orientation of <111> and consequently these techniques cannot be used in multicrystalline wafers. However, multicrystalline wafers can be textured using a photolithographic technique as well as mechanically sculpting the front surface using dicing saws or lasers to cut the surface into an appropriate shape. A micrograph of a photolithographic texturing scheme is shown below.

Scanning electron microscope photograph of a textured multicrystalline silicon surface.